Separation of copper and lead is a major problem when the flotation of copper-zinc ores lead. The solution can be lead-free copper or copper-lead. The exact plan is better and should be determined through specific tests. However, the general principle is: when the content of lead in the ore is much higher than that of copper, the lead should be suppressed; if the copper content is close to or more than lead, the lead should be suppressed.
Common copper and lead separation methods are as follows:
A heavy chromate method: i.e. dichromate suppress flotation of copper minerals and galena.
Second, the cyanidation method: the use of cyanide to inhibit copper minerals and flotation of lead minerals.
Third, the ferricyanide method: when the secondary high copper content in the ore, the effects of the two methods are not good enough, then if a high copper content in the ore, the available ferricyanide (ferrocyanide and Red blood salt) to inhibit the secondary copper mineral flotation lead mineral; if the lead content is much higher than copper, the following two options should be tested:
4. Sulfuric acid method (sulphur dioxide method): The mixed concentrate is treated with sulfur dioxide gas or sulfurous acid, so that the lead mineral is inhibited and the copper mineral is activated. In order to strengthen the inhibition, potassium dichromate or zinc dithionite may be added, or the slurry may be heated (heated flotation method), and finally the pH of the slurry must be adjusted to 5-7 with lime, and then copper is used. Flotation of minerals.
5. Sodium sulfite Ferric sulphate method: Sodium sulfite and iron sulphate are used as mixed inhibitors, and the slurry is acidified with sulfuric acid, stirred at pH=6-7, and the galena is inhibited to float the copper mineral.
One of the main reasons for the difficulty in separating copper-lead mixed concentrates is due to the presence of excess chemicals ( collectors and foaming agents) in the mixed concentrate. Removal of excess agent from the slurry prior to separation of the concentrate and removal of the collector film from the mineral surface can greatly improve the separation of the mixed concentrate.
Methods for removing excess pesticide from the slurry and removing the collector film from the mineral surface are:
(1) a mechanical method;
(b) Chemical or physicochemical methods. The appropriate method can be selected depending on the nature of the mixed concentrate and the conditions it obtains.
Boiler Tubes Erosion Shields
The anti-wear tile is mainly used on the windward side of the heating surface pipes such as the superheater, reheater, economizer, and water-cooled wall pipes of the boiler, as well as the induced draft fan (the amount is very small). Wind surface, reduce pipe wear and increase the service life of heating surface pipes. In the general industry, it is mostly called "anti-wear tile" and "anti-wear cover plate". Anti-abrasion tiles are special accessories for boilers. Generally, they are mostly used in power station boilers, and are used less in small boilers.
Lined With High Chromium Bimetal Composite Pipe,Bimetallic Lined With High Chrome Alloy Pipe,Bimetal Wear-Resisting Compound Pipe,Bimetallic Clad Pipe
Jiangsu Jianghe Machinery Manufacturing Co., Ltd. , https://www.jhceramiclinedpipe.com
![<?echo $_SERVER['SERVER_NAME'];?>](/template/twentyseventeen/skin/images/header.jpg)